PHILLYSTRAN® LASHING LINE PS29-LL180 |
146-2/06 |
| The PS29-LL180 lashing line is constructed of a twisted Kevlar® aramid fiber core with a black polyurethane extruded jacket. The low stretch, high modulus core provides a very high strength-to-weight ratio. The jacket provides maximum protection from ultraviolet light, fresh or salt water, outdoor weathering and long-term aging. The PS29-LL180 has excellent corrosion, chemical and abrasion resistance, plus excellent flexibility. |  |
|
CLICK HERE FOR PRINTER FRIENDLY PDF |
|
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Kevlar® is a Registered Trademark of DuPont | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| CAUTION: Break Strength: The breaking strength of a rope is the load at which a new rope will break when tested under laboratory conditions. Break strength should not be mistaken for safe working load. Safe Working Load: Because of the wide range of rope use, rope condition and the degree of risk of life or property, it is not possible to make a blanket recommendation for safe working load. It is ultimately dependent on the rope user to determine what percentage of break strength is their own safe working load. Wear: Ropes wear out with use; the more severe the usage, the greater the wear. It is often not possible to detect wear on a rope by visible signs alone. Therefore, it is recommended that the rope user determine a retirement criteria for ropes in their application. For assistance in developing safe working load and retirement criteria for each application please call or write Phillystran, Inc. All printed statements, data and recommendations are based on reliable information and tests, and are presented without any guarantee or warranty. Statements regarding the use of Phillystran, Inc.'s products and processes are not to be construed as recommendations for use in violation of any applicable laws, regulations or patent rights. © All rights reserved. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|